Publicación Restringido Comparison of descaling methods to study the corrosion kinetics of ferritic steels after dynamic exposure to molten carbonates(Elsevier, 2022-12-24) Audigié, P.; Rodríguez, Santiago; Agüero, A.; Pedrosa, Fátima; Paiva, Teresa; Diamantino, Teresa C.T91 ferritic-martensitic steel was exposed to Li, Na and K molten carbonates at 650ºC under dynamic conditions up to 1000 h. After testing, three descaling methods, two from the ISO8407 and one from the ISO17245 standards were applied to remove the corrosion products and determine the corrosion rates. The two ISO8407 methods were more appropriate although the procedure required several steps to fully remove the corrosion products. The ISO17245 method led to a higher mass loss affecting probably the base material. Oxides identification was performed by XRD following step by step layers removal. Li-, Na-, K-containing oxides and chromates/chromites were detected.